Precise geometry
A hardness of 255 HV10 helps maintain the precise geometry of the milled framework.
MESA MAGNUM SOLARE – Co-Cr-Mo CAD/CAM Milling Disc
€181,50
€150,00 excl. VAT
Price incl. VAT · VAT invoice with every order
DPD / UPS courier delivery · usually 2–7 business days
EU companies with a valid VAT number buy without VAT – enter your VAT number at checkout.
MESA MAGNUM SOLARE – a cobalt-chromium-molybdenum (Co-Cr-Mo) CAD/CAM disc for dental lab milling machines. The alloy is classified as Type 4 according to ISO 22674 and is suitable for single crowns as well as long-span bridges, with or without ceramic veneering, and...
Description- Consultations
- Help choosing the configuration and materials
- Delivery
- In Lithuania, the Baltic states and worldwide
Questions about this product?
Our product specialist will help you choose the right configuration.
Description
MESA MAGNUM SOLARE – a cobalt-chromium-molybdenum (Co-Cr-Mo) CAD/CAM disc for dental lab milling machines. The alloy is classified as Type 4 according to ISO 22674 and is suitable for single crowns as well as long-span bridges, with or without ceramic veneering, and for implant-supported restorations.
The disc is designed for dry milling, so no coolant is required and the lab workflow is simpler. A hardness of 255 HV10 and good machinability help achieve accurate framework geometry. The discs have a diameter of Ø 98,5 mm and are available in different heights.
- Type 4 Co-Cr-Mo alloy according to ISO 22674
- Hardness 255 HV10
- For crowns, bridges and implant-supported restorations
- Dry milling without coolant
- Diameter Ø 98,5 mm, several height options
Versatile use
Suitable for crowns, bridges and implant-supported structures, with or without ceramic veneering.
Dry milling
The disc is designed for milling without coolant, making the workflow simpler.
Good machinability
Good machinability, as stated by the manufacturer, makes milling and finishing easier.
Technical data
- Composition
- Co-Cr-Mo
- Type according to ISO 22674
- Type 4
- Solidus–liquidus temperature
- 1307–1417 °C
- Coefficient of thermal expansion
- 14,3–14,5 × 10⁻⁶ K⁻¹ (25–500/600 °C)
- Casting temperature
- 1470 °C
- Density
- 8,4 g/cm³
- Hardness
- 255 HV10
- Elongation at break
- 11 %
- Yield strength (Rp0,2)
- 395 MPa
- Diameter
- Ø 98,5 mm