High strength
A Type 5 alloy according to ISO 22674, suitable for reliable frameworks, including long-span bridges.
MESA MAGNUM Ceramic Co – Co-Cr-W-Mo Alloy for Metal-Ceramics
€242,00
€200,00 excl. VAT
Price incl. VAT · VAT invoice with every order
DPD / UPS courier delivery · usually 2–7 business days
EU companies with a valid VAT number buy without VAT – enter your VAT number at checkout.
MESA MAGNUM Ceramic Co – a cobalt-chromium-tungsten-molybdenum (Co-Cr-W-Mo) dental alloy for ceramic-veneered crown and bridge frameworks. It is classified as a Type 5 alloy according to ISO 22674, offering high strength and rigidity.The alloy is intended for dental technicians producing fixed prosthesis...
Description- Consultations
- Help choosing the configuration and materials
- Delivery
- In Lithuania, the Baltic states and worldwide
Questions about this product?
Our product specialist will help you choose the right configuration.
Description
MESA MAGNUM Ceramic Co – a cobalt-chromium-tungsten-molybdenum (Co-Cr-W-Mo) dental alloy for ceramic-veneered crown and bridge frameworks. It is classified as a Type 5 alloy according to ISO 22674, offering high strength and rigidity.
The alloy is intended for dental technicians producing fixed prosthesis frameworks by conventional casting. It contains no nickel, cadmium or beryllium, making it suitable for patients sensitive to these elements. Good machinability and relatively low density make framework finishing easier.
- Type 5 Co-Cr-W-Mo alloy according to ISO 22674
- For metal-ceramic crown and bridge frameworks
- Nickel-, cadmium- and beryllium-free
- Easy to machine, corrosion-resistant
- Pack – 1 kg
Nickel-, cadmium- and beryllium-free
Suitable for patients sensitive to these metals.
Good machinability
The casting is easy to finish and prepare for ceramic layering.
Corrosion resistance
A stable composition maintains surface quality in the oral environment for a long time.
Technical data
- Composition
- Co-Cr-W-Mo
- Type according to ISO 22674
- Type 5
- Purpose
- Frameworks for metal-ceramic crowns and bridges
- Solidus–liquidus temperature
- 1309–1417 °C
- Coefficient of thermal expansion
- 14,1–14,6 × 10⁻⁶ K⁻¹ (25–500/600 °C)
- Casting temperature
- 1470 °C
- Density
- 8,8 g/cm³
- Hardness
- 286 HV10
- Elongation at break
- 10 %
- Yield strength (Rp0,2)
- 570 MPa
- Flexural modulus
- 194 GPa
- Pack
- 1 kg